Pt@MOF‐177: Synthesis, Room‐Temperature Hydrogen Storage and Oxidation Catalysis

The gas-phase loading of [Zn(4)O(btb)(2)](8) (MOF-177; H(3)btb=1,3,5-benzenetribenzoic acid) with the volatile platinum precursor [Me(3)PtCp'] (Cp'=methylcyclopentadienyl) was confirmed by solid state (13)C magic angle spinning (MAS)-NMR spectroscopy. Subsequent reduction of the inclusion compound [Me(3)PtCp'](4)@MOF-177 by hydrogen at 100 bar and 100 degrees C for 24 h was carried out and gave rise to the formation of platinum nanoparticles in a size regime of 2-5 nm embedded in the unchanged MOF-177 host lattice as confirmed by transmission electron microscopy (TEM) micrographs and powder X-ray diffraction (PXRD). The room-temperature hydrogen adsorption of Pt@MOF-177 has been followed in a gravimetric fashion (magnetic suspension balance) and shows almost 2.5 wt % in the first cycle, but is decreased down to 0.5 wt % in consecutive cycles. The catalytic activity of Pt@MOF-177 towards the solvent- and base-free room temperature oxidation of alcohols in air has been tested and shows Pt@MOF-177 to be an efficient catalyst in the oxidation of alcohols.