Dual‐Site Cation Codoping Strategies Mitigating H2–H3 Phase Transition for Cycle Stable Nickel‐Rich Layered Oxide Cathodes in Lithium Batteries

This is the authors' abstract. We don't add key points for this paper.

Layered Ni‐rich transition metal oxide cathodes (LiNi 0.65 Mn 0.1 Co 0.25 O 2 ‐NMC) continue to dominate the market owing to the demand for high‐energy‐density lithium‐ion batteries. However, these cathodes suffer from rapid capacity and voltage decay during high voltage operation (≤4.5 V) due to unavoidable cation disorder (Li + /Ni 2+ ) and H2 → H3 phase transformation, inflicting structural instability. Herein, dual‐site cation doping using Mg 2+ in Li 3 a sites and Zr 4+ in transition metal‐T M (preferably Ni sites) 3 b sites is shown to preserve structure at high voltage, improving capacity retention and voltage fade. The Rietveld refinement of diffraction data shows that cation disorder reduced from ≈11% (NMC) to ≈2.9% (ZrMg‐NMC) with a low defect formation energy (Δ E ) of NMC (≈202.33 meV), favoring the formation of antisite defects. Cyclic voltammogram confirms that codoping prevents the H2 → H3 transformation at high voltage (≤4.5 V), reflected in better capacity retention (ZrMg‐NMC: ≈85%, vs. NMC: ≈51% at 200 cycles during cycling at 0.1C) and sluggish average voltage fading rate (ZrMg‐NMC: ≈0.12 mV/cycle, vs. NMC: ≈0.22 mV/cycle). The remarkable performance improvement by Zr–Mg codoping in NMC stems from preventing oxygen migration to the surface, dissuading rock salt phase formation, and stronger NiO and NiT M bond lengths, immensely helping to retain structural stability during charging up to 4.5 V.