Tetrahedral Zn2+ doping LiNi0.6Mn0.2Co0.2O2 improves discharge capacity retention by altering surface Ni valence during cycling and preventing oxygen evolution

5 mol-% Zn 2+ was added to the co-precipitation synthesis of LiNi 0.6 Mn 0.2 Co 0.2 O 2 (NMC622) to understand Zn's effect on the structural and electronic properties of NMC622. Zn is determined to successfully dope into the NMC crystal lattice as there is an increase in d -spacing along the [003], [104], and [110] directions and an increase in molar volume (100.75 cm 3 mol -1 for NMC622 and 101.00 cm 3 mol -1 for Zn-NMC). Through XPS, Zn is determined to dope on the tetrahedral 6c Wyckoff site in the NMC structure and TEM-EDS reveals that despite a slight ZnO impurity phase, 1.4 mol-% Zn successfully dopes into the crystal structure. Furthermore, cyclic voltammetry shows a suppressed anodic wave associated with oxygen evolution and EIS demonstrates that Zn-doped NMC decreases charge transfer resistance and increases Li diffusion by an order of magnitude. After the formation cycles, NMC has a higher 1 C accessible capacity, 141 mAh/g, over Zn-NMC (132 mAh/g), but after long term cycling Zn-NMC has a higher accessible capacity (117 mAh/g compared to 96 mAh/g for NMC) and increases discharge capacity retention by 18% leading to longer cycle life. • Tetrahedral Zn doping alleviates electrostatic repulsion preventing oxygen evolution. • Zn-NMC increases capacity retention by 18% leading to longer cycle life. • Zn doping increases Li diffusion and decreases SEI and charge transfer resistance.