This investigation elucidates the elevated-temperature (650 °C) monotonic mechanical response and very-high-cycle fatigue (VHCF) characteristics of Inconel 718 superalloys additively manufactured via selective laser melting (SLM), with a comparative assessment between the as-built and post-process heat-treated states. The results indicate that mechanical performance improves after heat treatment, primarily due to the formation of γ′ and γ″ precipitates, which interact with dislocations to strengthen the alloy. Relative to the as-built specimens, the fatigue strength of the specimen after heat treatment has increased by more than twice. For the as-built specimen, fatigue cracks nucleate at the specimen surface. However, in the high stress range, crack initiation in the heat-treated specimens consistently occurs at the free surface, whereas under low stress conditions, the crack initiation site transitions to the subsurface region encompassing internal defects. Post heat treatment, the fatigue crack trajectory adopts a markedly ductile and tortuous morphology, engendered by the concerted influence of grain-boundary (Laves/δ) precipitates that enforce repeated crack deflection, matrix-strengthening phases that homogenize plastic strain and the attendant reduction in local strain accumulation under the effect of cyclic load.
Song et al. (Tue,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: