Imaging of polymer:fullerene bulk-heterojunctions in a scanning electron microscope: methodology aspects and nanomorphology by correlative SEM and STEM

Scanning transmission electron microscopy (STEM) at low energies (≤ 30 keV) in a scanning electron microscope is well suited to distinguish weakly scattering materials with similar materials properties and analyze their microstructure. The capabilities of the technique are illustrated in this work to resolve material domains in PTB7:PC 71 BM bulk-heterojunctions, which are commonly implemented for light-harvesting in organic solar cells. Bright-field (BF-) and high-angle annular dark-field (HAADF-) STEM contrast of pure PTB7 and PC 71 BM was first systematically analyzed using a wedge-shaped sample with well-known thickness profile. Monte-Carlo simulations are essential for the assignment of material contrast for materials with only slightly different scattering properties. Different scattering cross-sections were tested in Monte-Carlo simulations with screened Rutherford scattering cross-sections yielding best agreement with the experimental data. The STEM intensity also depends on the local specimen thickness, which can be dealt with by correlative STEM and scanning electron microscopy (SEM) imaging of the same specimen region yielding additional topography information. Correlative STEM/SEM was applied to determine the size of donor (PTB7) and acceptor (PC 71 BM) domains in PTB7:PC 71 BM absorber layers that were deposited from solution with different contents of the processing additive 1,8-diiodooctane (DIO).