We demonstrate the synthesis of near-IR-emitting zinc blende CdTe/CdS tetrahedral-shaped nanocrystals with a magic-sized (approximately 0.8 nm radius) CdTe core and a thick CdS shell (up to 5 nm). These high-quality water-soluble nanocrystals were obtained by a simple but reliable aqueous method at low temperature. During the growth of the shell over the magic core, the core/shell nanocrystals change from type I to type II, as revealed by their enormous photoluminescence (PL) emission peak shift (from 480 to 820 nm) and significant increase in PL lifetime (from approximately 1 to approximately 245 ns). These thick-shell nanocrystals have a high PL quantum yield, high photostability, compact size (hydrodynamic diameter less than 11.0 nm), and reduced blinking behavior. The magic-core/thick-shell nanocrystals may represent an important step toward the synthesis and application of next-generation colloidal nanocrystals from solar cell conversion to intracellular imaging.
No takes yet. Share an insight, caveat, or question.
Deng et al. (2010) studied this question.
Synapse has enriched 10 related papers. Consider them for comparative context: