Research Progress in Lanthanum Extraction from Boehmite

The purpose of this study was to examine the utilization of 0–45 μm aluminum hydrate fraction (gibbsite) manufactured by Alum SA Tulcea, as a precursor in the hydrothermal synthesis process of nanosize boehmite from gibbsite suspensions. Furthermore, the use of the produced material as adsorbent of lanthanum (III) ions was investigated using aqueous solutions. Thermogravimetric analysis (TG), Fourier Transform InfraRed Spectroscopy (FT-IR), Wide-Angle X-Ray Scattering (WAXS), and atomic force microscopy (AFM) were used to demonstrate the preparation of the required material. Additionally, the material point of zero charge (pHpzc) and material specific surface (using BET approach) were evaluated. By conducting adsorption studies, the specific parameters for the lanthanum adsorption process were evaluated. The effects of pH, the ratio of adsorbent material to La(III) quantity from aqueous solution, contact time, and La(III) initial concentration were also assessed. Based on the obtained experimental data, it was proved that the maximum adsorption capacity of 97.7 mg/g was obtained for a solid:liquid ratio = 0.1 g:25 mL, pH between 3 and 6, temperature of 298 K, and contact time of 90 min. The studied adsorption process is most effectively described by the Sips model, suggesting an intricate interaction among the adsorbent material and La (III) ions. The prepared adsorbent exhibited a good desorption capacity (higher than 93%) when 20% HCl was used for desorption.