Oxidation-driven glass evolution enabling self-sealing protection in HfB ₂ -based boride–silicide coatings at high temperatures

At high temperatures, oxidation is generally regarded as an unavoidable degradation process for ceramic protective coatings. Here, oxidation is shown to drive dynamic glass evolution and form a robust self-sealing barrier under extreme thermal conditions. An in situ alloyed boride-silicide composite coating is constructed, and the controlled incorporation of HfSi₂ is found to change oxide-scale development by providing additional Hf and Si sources during oxidation and promoting the early formation and continuous reconstruction of a highly sealing Hf-Si-O glassy layer. The optimized coating exhibits exceptional oxidation resistance at 1700 °C, with oxygen permeability and carbon loss rate reduced by 61.67% and 75.26%, respectively, corresponding to an average protection efficiency of 99.94%. Mechanistically, oxidation-driven glass evolution seals pores and microcracks and slows inward oxygen diffusion, whereas appropriate HfSi₂ incorporation helps compact and stabilize the glassy layer, while excessive glass stiffening reduces high-temperature fluidity and weakens scale integrity. These findings provide a general design method for improving self-sealing oxidation protection at high temperatures.