High-Temperature Tribological Behavior of CrAlN/CrAlN-Ag Composite Coatings

To further improve the high-temperature dry sliding performance of Si3N4 ceramics, a CrAlN transition layer was introduced to improve interfacial stability, while Ag was incorporated as a solid lubricant into the CrAlN matrix. The effects of Ag content on the microstructure and mechanical properties of the coatings were systematically examined, and the tribological performance was evaluated from 25 °C to 550 °C under dry sliding conditions. The Ag concentration increased with increasing Ag target power and affected the morphology, nanoparticle distribution, surface roughness, and mechanical properties of the coatings. Among the tested samples, the coating containing 9.6 at.% Ag exhibited a comparatively favorable combination of mechanical properties within the investigated composition range, with a hardness of 11.5 GPa, an H/E ratio of 0.0913, and an H3/E2 value of 0.096 GPa. Tribological tests showed that the average coefficient of friction decreased from 0.32 at 25 °C to 0.12 at 550 °C. This reduction may be associated with temperature-assisted Ag redistribution toward the worn surface and the possible development of Ag-rich surface features at elevated temperatures. However, the wear rate increased with temperature, reaching 3.6 × 10−5 mm3/(N·m) at 550 °C, suggesting that friction reduction was accompanied by increased material removal and possible near-surface weakening. These results indicate that controlling Ag content is important for balancing friction reduction and wear resistance in ceramic-based self-lubricating coatings.