High Electron Mobility and Ambipolar Transport in Organic Thin‐Film Transistors Based on a π‐Stacking Quinoidal Terthiophene

Thin‐film transistors (TFTs) based on a new n‐channel organic semiconductor (DCMT; see Figure) are reported. An electron mobility as high as 0.2 cm 2 /V s was observed, as well as ambipolar TFT behavior. Variable temperature measurements reveal that electron conduction is activated, with a small activation energy of 35 ± 10 meV. These results demonstrate that quinoidal oligothiophenes are a promising new class of organic semiconductors for TFTs.