Morphology Matters: Tuning the Product Distribution of CO2 Electroreduction on Oxide-Derived Cu Foam Catalysts

Mesoporous Cu foams formed by a template-assisted electrodeposition process have been identified as CO2 electrocatalysts that are highly selective toward C2 product formation (C2H4 and C2H6) with C2 efficiencies (FEC2) reaching 55%. The partial current of C2 product formation was found to be higher than that of the (parasitic) hydrogen evolution reaction (HER) at any potential studied (−0.4 to −1.0 vs the reversible hydrogen electrode). Moreover, formate production could largely be suppressed at any applied potential down to efficiencies (FEformate) of ≤6%. A key point of the Cu foam catalyst activation is the in operando reduction of a Cu2O phase, thereby creating a large abundance of surface sites active for C–C coupling. The cuprous oxide phase has been formed after the Cu electrodeposition step by exposing the large-surface area catalyst to air at room temperature. The superior selectivity of the Cu foam catalyst studied herein originates from a combination of two effects, the availability of specific surface sites for C–C coupling dominant (100) surface texture and the temporal trapping of gaseous intermediates (in particular CO and C2H4) inside the mesoporous catalyst material during CO2 electrolysis. A systematic CO2 electrolysis study reveals a strong dependence of the C2 efficiencies on the particular surface pore size of the mesoporous Cu catalysts with a maximal FEC2 between 50 and 100 μm pore diameters.