An appropriate solution is suggested for synthesizing wafer-scale, continuous, and stoichiometric MoS2 layers with spatial homogeneity at the low temperature of 450 °C. It is also demonstrated that the MoS2-based visible-light photodetector arrays are both fabricated on 4 inch SiO2/Si wafer and polyimide films, revealing 100% active devices with a narrow photocurrent distribution and excellent mechanical durability. As a service to our authors and readers, this journal provides supporting information supplied by the authors. Such materials are peer reviewed and may be re-organized for online delivery, but are not copy-edited or typeset. Technical support issues arising from supporting information (other than missing files) should be addressed to the authors. Please note: The publisher is not responsible for the content or functionality of any supporting information supplied by the authors. Any queries (other than missing content) should be directed to the corresponding author for the article.
Lim et al. (Wed,) studied this question.