Al2O3 single beads were deposited on a Ti-6Al-4V (Ti64) substrate by laser-directed energy deposition (DED-LB) to establish baseline process conditions for ceramic protective layers and future Ti64/Al2O3 functionally graded materials (FGMs). These ceramic-containing surface layers are applicable to titanium components requiring improved oxidation, wear, and thermal resistance in aerospace, automotive, and high-temperature structural applications. Laser power (300–700 W) and scan speed (300–700 mm/min) were varied, and bead geometry was quantified from cross-sectional observations; energy density and dilution ratio were calculated. Melt pool depth increased with higher power and lower speed, indicating increased heat input and substrate melting. Crack formation in the melt zone was more sensitive to laser power than to scan speed. In contrast, bead height showed a non-monotonic response to energy density, which may be associated with possible coupled effects such as recoil pressure-driven melt pool disturbance, powder scattering, and insufficient powder melting at high scan speeds. Dilution-based optimization identified 300 W laser power and 400 mm/min scan speed, with a powder feed rate of 3 g/min, as the most suitable condition within the investigated process window, giving the lowest practical dilution ratio of approximately 40.27%. SEM–EDS and XRD analyses were conducted to examine the interfacial microstructure and phase characteristics under the selected condition. Overall, this study provides fundamental process guidelines and mechanistic insight into bead formation, dilution behavior, and interface formation, supporting the future application of DED-LB-based ceramic protective or graded layers on Ti64 surfaces.
Kim et al. (Tue,) studied this question.