High Tg Cyclic Olefin Copolymer Gate Dielectrics for N,N′‐Ditridecyl Perylene Diimide Based Field‐Effect Transistors: Improving Performance and Stability with Thermal Treatment

A novel application of ethylene‐norbornene cyclic olefin copolymers (COC) as gate dielectric layers in organic field‐effect transistors (OFETs) that require thermal annealing as a strategy for improving the OFET performance and stability is reported. The thermally‐treated N , N′ ‐ditridecyl perylene diimide (PTCDI‐C13)‐based n‐type FETs using a COC/SiO 2 gate dielectric show remarkably enhanced atmospheric performance and stability. The COC gate dielectric layer displays a hydrophobic surface (water contact angle = 95° ± 1°) and high thermal stability (glass transition temperature = 181 °C) without producing crosslinking. After thermal annealing, the crystallinity improves and the grain size of PTCDI‐C13 domains grown on the COC/SiO 2 gate dielectric increases significantly. The resulting n‐type FETs exhibit high atmospheric field‐effect mobilities, up to 0.90 cm 2 V −1 s −1 in the 20 V saturation regime and long‐term stability with respect to H 2 O/O 2 degradation, hysteresis, or sweep‐stress over 110 days. By integrating the n‐type FETs with p‐type pentacene‐based FETs in a single device, high performance organic complementary inverters that exhibit high gain (exceeding 45 in ambient air) are realized.