Mechanical, Thermal and Microstructural Characteristic of 3D Printed Polylactide Composites with Natural Fibers: Wood, Bamboo and Cork

Abstract In the study, polylactide-based (PLA) composites modified with natural particles (wood, bamboo, and cork) and with different levels of infilling (100%, 80%, and 60%) obtained by fused deposition modeling were tested. The effect of fiber type, infill level and crystallization rate on the mechanical properties were investigated by using tensile, flexural, and impact tests. The materials were subjected to mechanical tests carried out at 23 and 80 °C. Differential scanning calorimetry were employed to analyze crystallization behavior of composite. Furthermore, hydrothermal degradation was performed, and its effect on the properties was analyzed. The addition of natural fillers and different levels of infilling result in a similar level of reduction in the properties. However, the addition of natural fillers resulted in a slightly lower drop than the lowered infilling rate − 40% and 50% for tensile strength, respectively. Moreover, it was found that, composites made of PLA are more sensitive to high temperatures than to water. The decrease in Young's modulus of PLA at 80 °C was 90%, while after 28 days of hydrodegradation ~ 9%. The addition of fibers reduced this decrease at elevated temperatures. Importantly, in the case of a brittle material such as PLA, the impact strength has been improved by 50% for composites with cork particles and other lignocellulosic composites remained at the same level as for resin. Generally, the thermal treatment of composites increased the degree of crystallinity of the materials, as reflected in the higher results of mechanical tests.