Noise Control Using Coconut Coir Fiber Sound Absorber with Porous Layer Backing and Perforated Panel

Problem statement: Noise control was one of the major requirements to improve the living environment. One of the methods to do that is provided by sound absorber. Commonly, multi-layer sound absorbers are applied to absorb broadband noise that was composed of perforated plates, air space and porous material. However, multi-layers sound absorbers effectiveness depends on their construction. This study was conducted to investigate the potential of using coconut coir fiber as sound absorber. The effects of porous layer backing and perforated plate on sound absorption coefficient of sound absorber using coconut coir fiber were studied. Approach: Car boot liners made from woven cotton cloth were used as type of porous layer in the study. This material has been used widely in automotive industry. Perforated plate used was machined with perforation ratio of 0.20, thickness of 1 mm and holed diameter of 2 mm. The samples were tested at the acoustic lab of the Faculty of Engineering and Built Environment, University Kebangsaan Malaysia, according to ASTM E 1050-98 international standards for noise absorption coefficient. Results: The experiment data indicates that porous layer backing can improve noise absorption coefficient at low and high frequencies with significant increasing. 20 mm thick layer coconut coir fiber with porous layer backing exhibit peak value at frequencies between 2750-2825 Hz with maximum value of 0.97. The experimental results also found that the coconut coir fiber with perforated plate gives higher value for lower frequencies range from 600-2400 Hz. The optimum value for coconut coir fiber with perforated panel is around 0.94-0.95 for the frequency range 2600-2700 Hz. Conclusion: Noise absorption coefficient of coconut coir fiber was increased at all frequency when they were backing with Woven Cotton Cloth (WCC). At low frequency, the NAC have significant increasing. This is because WCC have higher flow resistivity than coconut coir fibers, so that sound can be dissipated as it travels through material significantly. The results from the experimental tests show that it has good acoustic properties at low and high frequencies and can used to be an alternative replacement of synthetic based commercial product. By using the porous layer and perforated plate backing to coconut coir fiber, the sound absorber panel shows a good potential to be an environmentally friendly product. This innovative sound absorption panel has a bright future because they are cheaper, lighter and environmentally compare to glass fiber and mineral based synthetic materials.