Study on Deep Vanadium Extraction and Calcified Dealkalinization of Vanadium Extraction Residue

Vanadium extraction tailings, as a highly alkaline and hazardous solid waste, pose not only serious environmental risks but also severely hinder the large-scale recycling of secondary iron resources. This study proposes an innovative process of “mild alkali leaching for vanadium extraction coupled with deep calcification and dealkali removal”. The vanadium extraction slag from a steel plant in China was used as a raw material to carry out the experimental and pilot study of alkali leaching of vanadium and calcification dealkalization. Experimental results show that under the conditions of 120 °C, 1% NaOH solution, liquid-solid ratio of 4:1 to 6:1, and reaction time of 1 h, vanadium leaching rate can reach 50%, which can be effectively used as a high-value-added economic hedge. Subsequently, under the conditions of 200 °C, calcium oxide concentration of 19.29%, stirring speed of 800 rpm, liquid-solid ratio of 4:1, and reaction time of 1 h, the Na2O content in the tailings was successfully reduced to below 1%. A large number of tailings can be converted into high-quality secondary iron ore resources, which are suitable for subsequent iron-bearing briquette preparation and blast furnace ironmaking. Furthermore, pilot-scale testing in a 200 L reactor verified the engineering scalability of this combined process, maintaining a vanadium extraction rate of over 50% and an alkali removal rate of over 80%. This study provides a robust, scalable, and highly profitable pathway for the comprehensive utilization of high-alkali metallurgical solid waste.