CuO@ZnO Nanocomposites with Improved Redox Behavior for High-Performance Supercapacitors

In this work, we employed an easy hydrothermal method to prepare CuO and ZnO, as well as the prepared composite nanostructured electrodes of CuO@ZnO for supercapacitor applications. The systematic electrochemical performance evaluation of the prepared materials was conducted by cyclic voltammetry (CV), galvanostatic charge–discharge (GCD), and electrochemical impedance spectroscopy (EIS). CuO@ZnO nanocomposite reflected the best charge storing behavior with a specific capacitance of 513 F/g, followed by pristine CuO (190 F/g) and ZnO (416 F/g). The composite also demonstrated 25.67 Wh/kg and 400 W/kg for energy density and power density, respectively, suggesting improved electrochemical performance. Besides, the areal and volumetric capacitances were 0.77 F/cm2 and 4.81 F/cm3, respectively, supported by the structural integrity and enhancement in electroactive materials utilization of the electrode material. Kinetic analysis showed that b values of the samples had mixed capacitive/diffusion-controlled charge storage, while higher diffusion coefficients and standard rate constants were apparent for ion transport or redox kinetics. EIS results showed a 2.14 Ω solution resistance, indicative of a decreased electrical resistivity. An asymmetric supercapacitor device fabricated by CuO@ZnO as the positive electrode and activated carbon (AC) as the negative electrode provided the specific capacitance of 48.57 F/g, energy density of 15.17 Wh/kg, and power density of 535 W/kg. After 10,000 cycles, the capacitance of the device was 76%, indicating good long-term stability.