Effect of Heat Input on Microstructure and High-Cycle Fatigue Properties of the CGHAZs in Wind Power Steel

Wind turbine towers rely on welded joints for structural continuity, and the coarse-grained heat-affected zone (CGHAZ) at these joints is the principal site of fatigue damage under service loading. This study characterises the influence of welding heat input on the microstructural constitution, high-cycle fatigue response, and fracture mechanisms of Gleeble-simulated CGHAZs in a Nb-microalloyed wind power steel. Thermal cycles representative of submerged arc welding at 15, 25, 35, and 45 kJ/cm were applied, and the resulting microstructures were examined by optical microscopy, SEM, EBSD, and TEM. Raising the heat input produced systematic microstructural coarsening: the densities of low-angle grain boundaries (LAGBs) and high-angle grain boundaries (HAGBs) fell by approximately 40% and 26%, respectively, while the mean equivalent diameter (MED) and prior austenite grain (PAG) size grew by roughly 64% and 67%. Life partitioning showed that crack nucleation accounted for more than 84% of total fatigue cycles in every condition, identifying it as the life-governing damage stage. Over the 15-to-45 kJ/cm range, the CGHAZ fatigue strength at 2 × 106 cycles deteriorated from 246.9 MPa to 208.5 MPa (a 15.6% reduction), while the mean fatigue striation spacing widened from 0.142 μm to 0.183 μm (an increase of 28.9%). These results demonstrate that judicious heat-input selection is a practical and effective means of preserving CGHAZ fatigue integrity in wind tower steel fabrication, and they address a previously unresolved gap concerning high-cycle fatigue fracture mechanisms in this critical microstructural zone.