Plasma Transferred Arc Deposition of Ni–Cr–B–Si–WC Composite Coatings on Steel 45: Effect of Arc Current on Microstructure, Phase Composition, Hardness, and Tribological Performance for Roller Mill Roll Restoration

Worn roller mill roll shafts made of Steel 45 require cost-effective surface restoration; plasma transferred arc (PTA) deposition of Ni–Cr–B–Si + WC composite coatings is a promising approach, yet the effect of arc current on coating quality remains insufficiently characterised for this substrate. Six coatings were deposited from PS-12NVK-01 powder (65 wt.% PG-10N-01 + 35 wt.% WC) at arc currents of 50–100 A on Steel 45 substrates using a ZTW3501DC PTA system; coatings were characterised by SEM, EDS mapping, XRD (HighScore Plus, PDF-2), Vickers microhardness profiling, and ball-on-flat tribological testing. EDS analysis revealed that compositional dilution increases from 18.1% at 60 A to 46.6% at 100 A; XRD identified WC + Cr3C2 + Ni3B + Ni2B + (Fe,Ni)γ at 50 A, transitioning through Cr7C3 + W2C dominance at 80 A to an Fe0.64Ni0.36 matrix at 100 A; and coating thickness peaked at 2.70 mm at 80 A. The 60 A coating yielded the highest surface hardness (887 ± 76 HV, >4× the substrate), the lowest specific wear rate (4.00 × 10−6 mm3/(N·m), ~22× lower than uncoated Steel 45), and minimum dilution (18.1%), identifying 60 A as the most favourable deposition current for the restoration of roller mill roll shafts under the process parameters employed.