Synergistic Enhancement of Corrosion Resistance of GO/LDH Coating on Anodized Magnesium Alloy Surfaces via pH-Regulated In Situ Growth and Anionic Corrosion Inhibitor Intercalation

Magnesium alloys offer low density, high strength, excellent heat dissipation, and good electrical conductivity, benefiting automotive and aerospace sectors. However, magnesium and its alloys are highly susceptible to corrosion, which severely limits their practical use. In this study, the hydrothermal deposition of graphene oxide (GO) and layered double hydroxides (LDHs) was achieved on the surface of an anodized magnesium alloy, forming a GO/LDH coating. The effects of pH and various anionic corrosion inhibitors on the corrosion resistance of the GO/LDH coating were subsequently investigated. The results show that the GO/LDH coating prepared at pH 10.8 exhibits the best corrosion resistance, which is generally associated with a greater coating thickness, with its nanosheets growing in a wavy manner in all directions. This coating also shows higher crystal transparency and a denser layered structure. Based on this, anionic corrosion inhibitors including molybdate, vanadate, and tungstate were incorporated into the GO/LDH coating. Electrochemical impedance (EIS) analysis subsequently revealed that the GO/LDH–molybdate coating exhibited the highest |Z|0.01 HZ, reaching ~105.5 Ω cm2, indicating its excellent corrosion resistance. This approach offers a novel and effective route to significantly improve the corrosion resistance of magnesium alloys via synergistic coating design.