A high-performance, biodegradable Zn-3Cu-0.8Sr alloy with superior strength, biotribology, osteogenesis, and antibacterial activity for orthopedic fixation through deep-cryogenic rolling

of ∼245.0 MPa, and ε of ∼33.5%, with minimal strength/ductility loss after 30-day immersion in Hanks' Balanced Salt Solution (HBSS). It demonstrates a favorable electrochemical corrosion rate (∼162 µm/y), degradation rate (∼20.1 µm/y), and superior biotribological resistance in Dulbecco's Modified Eagle Medium supplemented with fetal bovine serum (DMEM+FBS). Biologically, it enhances osteoblast viability and mineralization while providing near-complete S. aureus antibacterial efficacy in vitro and in vivo. This synergistic combination of strength, corrosion-wear resistance, and bioactivity highlights the alloy's significant potential for advanced biodegradable orthopedic applications.