Effect of Hot Rolling Temperature on the Microstructure and Macro-Texture Evolution Laws of TC2 Titanium Alloy and Their Influence on Mechanical Properties

TC2 titanium alloy (Ti-4Al-1.5Mn, wt.%) is a near-α titanium alloy with promising aerospace and biomedical applications, but its limited room temperature ductility and strong texture sensitivity hinder the fabrication of high-performance sheets. In this study, the effects of hot rolling at 830 °C and 930 °C on the microstructure, macro-texture, mechanical properties, and fracture behavior of TC2 alloy were investigated. Compared with the 830 °C rolled sample, the 930 °C rolled sample exhibited finer primary α grains, a higher volume fraction of fine and dispersed secondary αs phase, and more uniform Mn distribution, while both samples retained an α + β phase constitution. Texture and ODF (orientation distribution function) analyses revealed that increasing the rolling temperature reduced the maximum intensity of the (0001) pole figure from 6.68 to 5.23 m.r.d. (multiples of a random distribution) and increased that of the (10-10) pole figure to 9.62 m.r.d., indicating weakened basal texture, enhanced prismatic texture, and more dispersed orientation distribution. Consequently, although the tensile strength slightly decreased to approximately 730 MPa, the elongation increased from approximately 24% to 28%. The finer and denser dimples observed after 930 °C rolling further confirmed improved plastic deformation coordination.