Key points are not available for this paper at this time.
Abstract With a theoretical capacity of 847 mAh g −1 , Sn has emerged as promising anode material for sodium‐ion batteries (SIBs). However, enormous volume expansion and agglomeration of nano Sn lead to low Coulombic efficiency and poor cycling stability. Herein, an intermetallic FeSn 2 layer is designed via thermal reduction of polymer‐Fe 2 O 3 coated hollow SnO 2 spheres to construct a yolk‐shell structured Sn/FeSn 2 @C. The FeSn 2 layer can relieve internal stress, avoid the agglomeration of Sn to accelerate the Na + transport, and enable fast electronic conduction, which endows quick electrochemical dynamics and long‐term stability. As a result, the Sn/FeSn 2 @C anode exhibits high initial Coulombic efficiency (ICE=93.8 %) and a high reversible capacity of 409 mAh g −1 at 1 A g −1 after 1500 cycles, corresponding to an 80 % capacity retention. In addition, NVP//Sn/FeSn 2 @C sodium‐ion full cell shows outstanding cycle stability (capacity retaining rate of 89.7 % after 200 cycles at 1 C).
Chen et al. (Thu,) studied this question.