Soft magnetic composites (SMCs) are attracting increasing attention for electromagnetic applications owing to their three-dimensional shape flexibility and reduced eddy current loss. In this study, the 2-Pressing 1-Annealing (2P1A) process was applied to Fe–5.0 wt.%Si SMC toroidal cores to investigate the effects of pressing temperature and 1st pressing level on densification behavior, interparticle insulation structure, and frequency-dependent electromagnetic response. DEFORM-3D FEM simulations compared relative density distribution, hydrostatic stress, effective strain, and reaction load under single-press and 2P1A conditions. The 1st pressing stage was conducted at 350 °C with 30%, 50%, and 70% pressing levels, followed by final densification at 550 °C. Increasing compaction temperature reduced reaction load and hydrostatic stress range, while the 1st pressing level affected the final density distribution and stress state after 2nd pressing. TEM-EDS confirmed continuous interparticle insulation layers, and thickness measurements were used to compare local boundary structures. Among the 2P1A conditions, the 50% → 100% condition showed the smallest upper/lower relative density difference and the narrowest insulation-layer thickness range, indicating the most balanced condition in terms of densification uniformity and interparticle boundary structure. Compared with the 550 °C single-press condition, the 2P1A compacts showed higher permeability retention and Q-factor values in the 5–20 kHz range. These results indicate that the 1st pressing level influences staged densification behavior, interparticle boundary structure, and frequency-dependent electromagnetic response in Fe–5.0 wt.%Si SMC cores.
Sim et al. (Wed,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: