Effect of Laser Power on Microstructure and Mechanical Properties of GH4141 + 0.2 wt.% Y2O3 Alloy Fabricated by Laser Powder Bed Fusion

GH4141 + 0.2 wt.% Y2O3 superalloy was fabricated using laser powder bed fusion (LPBF) technology and subjected to solution and ageing heat treatments. The effects of laser power (1100, 1300, 1500 W) on the microstructure and mechanical properties of the ODS nickel-based superalloy were investigated. The results indicate that as the laser power increased from 1100 W to 1300 W, defects such as cracks and pores in the specimens decreased, the grains were refined, and the microstructure became more uniform; when the laser power was further increased to 1500 W, the grain size coarsened significantly, precipitation phases at the grain boundaries became coarser or locally aggregated, and crack sensitivity increased. EDS analysis revealed enrichment of C, Cr, Mo and Ti in the dark phases at the grain boundaries, which may be associated with MC-type and M23C6-type carbides; no significant agglomeration of Y2O3 particles was observed in the matrix. Room-temperature tensile properties exhibited a pattern of initially increasing and then decreasing with increasing laser power. The tensile strength and elongation after fracture of the specimens were relatively similar under 1100 W and 1500 W conditions, whilst the specimen tested at 1300 W achieved the optimal balance of strength and toughness, with a tensile strength of 1460 MPa and an elongation after fracture of 14.3%, representing increases of approximately 9.8% and 54% compared to the 1100 W and 1500 W conditions, respectively. At 760 °C, the 1300 W specimens still maintained excellent high-temperature strength.