Shifting valencies and magnetic responses in la-based high-entropy oxide perovskite thin films with variable Mn presence

Chemical disorder in compositionally complex perovskite oxides generates a broad distribution of exchange pathways and spin states, but the microscopic origin and spatial homogeneity of the resulting magnetic phases remain debated. Here, we tune the Mn fraction (x = 0.2–0.6) in epitaxial La(Cr, Mn, Fe, Co, Ni)O₃ thin films and resolve the coupled evolution of valence, spin state, and magnetism using element-specific x-ray absorption spectroscopy and x-ray magnetic circular dichroism (XMCD). Mn enrichment drives an internal redistribution of charge, in which Mn evolves toward a Mn³⁺-rich mixed valence, while Co converts from predominantly Co³⁺ to high-spin Co²⁺. This valence/spin-state coupling amplifies the Mn- and Co-derived ferromagnetic response by nearly an order of magnitude while increasing the magnetic onset temperature to at least 250 K, whereas Fe and Cr remain essentially trivalent with weak dichroism. Depth-resolved low-energy muon spin spectroscopy (LE-μSR) shows magnetic homogeneity through the film thickness, with a secondary relaxation maximum near 25 K indicating a low-temperature dynamical crossover consistent with frustrated magnetism in a strongly disordered spin lattice.