To address the pervasive engineering challenges of rigid interference and subpar machining efficiency encountered during the complex freeform surface polishing of P20 mold steel, this study proposes and fabricates a structurally designed, five-petal composite compliant polishing tool via fused granulation fabrication (FGF). The tool structurally integrates a passive thermoplastic polyurethane (TPU) compliant buffer layer with an active PA66/diamond micro-cutting functional layer, achieving monolithic precision assembly through dual-temperature-zone 3D printing. Tensile mechanical characterization (n = 6) reveals that the composite interface attains an average ultimate tensile strength (UTS) of 59.39 ± 15.41 MPa (with a peak of 78.90 MPa) and an average elongation at break of 27.42 ± 7.41%, demonstrating exceptional structural robustness and fracture toughness under heavy-load abrasive machining conditions. During adaptive polishing validations on complex convex topographies and deep concave mold cavities, the compliant tool effectively compensated for normal vector spatial errors intrinsic to three-axis CNC machining via passive geometric adaptation. Topographical evaluations suggest a ductile-regime, differential asperity planarization material removal paradigm, which is attributed to the macroscopic 3D elastic deformation of the tool synergized with the proposed compliance of the polymer matrix. Following high-intensity sequential polishing regimens, the original macroscopic milling striations were substantially reduced. Quantitative profilometric analysis reveals that the average surface roughness of the convex profiles decreased from an initial 13.33 µm to 7.42 µm, while that of the restrictive deep concave features was reduced from 10.84 µm to 4.11 µm. Ultimately, this technological framework circumvents the traditional reliance on capital-intensive, six-degree-of-freedom robotic platforms, providing a scalable automated polishing protocol compatible with standard CNC systems for the cost-effective surface planarization of precision molds.
Wang et al. (Thu,) studied this question.