The Role of Ferrite Kinetics and Strain Rate in Preventing Straightening Cracks During Continuous Casting: A Focused Review of Hot Tensile Testing

The paper presents a critical review of the key work published to date on the hot ductility of steels in relation to the problem of cracking during continuous casting, including recent publications in the field. Laboratory testing methods that are most appropriate for evaluating cracking susceptibility are examined, with particular emphasis on the hot tensile test. The discussion covers both conventional carbon–manganese (C–Mn) and high-strength low-alloy (HSLA) steels, as well as the more complex advanced high-strength steels. Special attention is given to the influence of strain rate and the role of ferrite, both transformation-induced and deformation-induced, in controlling ductility. Increasing the strain rate invariably improves the ductility of steels containing a thin film of ferrite when it is present. This improvement is attributed to the work hardening of the ferrite, which promotes a more uniform distribution of strain, rather than localisation within the thin ferrite layer, thereby reducing the likelihood of fracture. The difficulties in increasing the strain rate in continuous casters are cited. Finally, based on insights from tensile testing, the paper considers practical approaches to preventing cracking in conventional curved-mould and vertical-mould arc continuous casting machines. Newly designed chamfered moulds have also recently been introduced, and these are claimed to reduce the incidence of corner cracking; their role is also discussed.