Exploration of sub-bandgap states in 2D halide perovskite single-crystal photodetector

Abstract Greater stability of low-dimensional halide perovskites as opposed to their three-dimensional counterparts, alongside their high extinction coefficient and thus excellent emission properties, have made them popular candidates for optoelectronic applications. Topological edges are found in two-dimensional perovskites that show distinct electronic properties. In this work, using Kelvin Probe Force Microscopy, performed on butylammonium lead bromide (BA 2 PbBr 4 ) single crystals with optical bandgap of ~413 nm, we elucidate the electronic response of the edges and their potential impact on photodetector devices. We show that the charge-carriers are accumulated at the edges, increasing with the edge height. Wavelength-dependent surface photovoltage (SPV) measurements reveal that multiple sub-bandgap states exist in BA 2 PbBr 4 . As the edge height increases, the SPV amplitude at the edges reduces slightly more as compared to the adjacent regions, known as terraces, indicating relatively less reduction in band-bending at the surface due possibly to increased de-population of electrons from sub-bandgap states in the upper bandgap half. The existence of sub-bandgap states is further confirmed by the observation of below-bandgap emission (absorption) peaks characterised by spectral photoluminescence and photothermal deflection spectroscopy measurements. Finally, we fabricated a photodetector using a millimetre size BA 2 PbBr 4 single crystal. Noticeable broadband photodetection response was observed in the sub-bandgap regions under green and red illumination, which is attributed to the existence of sub-bandgap states. Our observations suggest edge-height dependence of charge-carrier behaviour in BA 2 PbBr 4 single crystals, a potential pathway that can be exploited for efficient broadband photodetector fabrication.