A series of semiaromatic polyimides containing polyhedral oligomeric silsesquioxane (POSS) in main chain (POSS−PIs) from a double-decker-shaped silsesquioxane diamine (DDSQ−diamine) ( 4 ) with various aromatic tetracarboxylic dianhydrides were prepared and the structures were characterized by IR and NMR spectra. A double-decker-shaped silsesquioxane dianhydride (DDSQDA) ( 3 ) was synthesized by hydrosilylation reaction from double-decker-shaped silsesquioxane (DDSQ) ( 1 ) and cis -5-norbornene- endo -2,3-dicarboxylic anhydride ( 2 ), which then reacted with 4,4‘-oxydianiline (ODA) to produce the DDSQ-diamine. The POSS−PIs possessed good thermal stability and mechanical properties, low water absorption, and alkali resistance as well as low dielectric constant. The 5% weight loss temperatures ( T d 5 ) in air were observed at 495−514 °C. The polymer films had good mechanical properties with elongation at breakage of 2.9−6.0%, in which POSS−PI 8c derived from 4,4‘-oxydiphthalic anhydride (ODPA) exhibits the highest elongation of 6.0%. The water absorption of POSS−PI 8b (<1%) was much lower than that of PI from pyromellitic dianhydride (PMDA)/ODA (6.0%). POSS−PIs 8 possessed excellent alkaline and acid resistance. POSS−PI 8b kept its flexible mechanical properties when immersed in 5% NaOH solution at 40 °C for 72 h. The dielectric constant of POSS−PI 8c measured by precision impedance method was 2.36.
Wu et al. (Wed,) studied this question.