Facile One-Pot Solvothermal Synthesis of the RGO/MWCNT/Fe₃O₄ Hybrids for Microwave Absorption

) and their multi-interfacial and porous structure. Also, the MA performance of the GMFs was conducted. The GMFs exhibited a maximum reflection loss (RL) value of -61.29 dB at 10.48 GHz with a thickness of 2.6 mm when the contents of RGO and MWCNT were 6.3 and 1.3 wt %, respectively. The RL values (≤-10 dB) were observed to be in the range of 8.96-12.32 GHz, and the effective microwave absorption bandwidth was tunable from 3.52 to 18 GHz by changing the sample thickness. The results revealed that the multi-interfacial and porous structure of the GMFs is beneficial to MA performance by inducing multiscatterings. Since no toxic solvents were used, this method is environmentally friendly and has potential for large-scale production. The prepared GMFs may have a wide range of applications in MA materials against electromagnetic interference pollution.