Increase in Electrical Conductivity of MOF to Billion-Fold upon Filling the Nanochannels with Conducting Polymer

Redox-active pyrrole (Py) monomers were intercalated into 1D nanochannels of Cd(NDC)0.5(PCA)·Gx (H2NDC = 2,6-napthalenedicarboxylic acid, HPCA = 4-pyridinecarboxylic acid, G = guest molecules) (1) - a fluorescent 3D MOF (λem = 385 nm). Subsequent activation of 1⊃Py upon immersing into iodine (I2) solution resulted in an increment of the bulk electrical conductivity by ∼9 orders of magnitude. The unusual increase in conductivity was attributed to the formation of highly oriented and conducting polypyrrole (PPy) chains inside 1D nanochannels and specific host-guest interaction in 1⊃PPy thereof. The Hall-effect measurements suggested 1⊃PPy to be an n-type semiconductor material with remarkably high-carrier density (η) of ∼1.5 × 10(17) cm(-3) and mobility (μ) of ∼8.15 cm(2) V(-1) s(-1). The fluorescence property of 1 was almost retained in 1⊃PPy with concomitant exciplex-type emission at higher wavelength (λem = 520 nm). The here-presented results on MOF⊃Conducting Polymer systems in general will serve as a prototype experiment toward rational design for the development of highly conductive yet fluorescent MOF-based materials for various optoelectronic applications.