The present paper reviews original data obtained by the authors from recent separate publications with additional unpublished data, specifically concerning the specific graphite morphology in Si/SiMo alloyed ductile irons (2.5–5.5% Si, 0.01–2.3% Mo) with alloying grade, cooling rate, and inoculation as influencing factors. Different formulas used for nodularity evaluation, including different forms of graphite participating in different proportion and two graphite shape factors: Roundness (RSF, involving maximum Ferret) and Sphericity (SSF, involving real perimeter). Slightly irregular spheroidal graphite morphology (Form V, ISO 945) characterized by RSF = 0.59–0.75 was found to be typical for Si and SiMo ductile irons in all of the test conditions, such as Si level (4.2–5.25% Si), Si–Mo system (4.1–4.8% Si + 1.6–2.3% Mo), mould type (green sand, resin sand, metal mould, external metallic chill), un-inoculation and inoculation, and inoculating element type. Increasing Si content negatively affects the compactness degree of spheroidal graphite particles (transition from VI to V form) and nodularity. Metal mould versus sand mould solidification of 4.5% Si ductile iron increases nodule count, graphite shape factors (RSF = 0.68–0.7 versus 0.59–0.64) and nodularity (67% to 76%). An external metallic chill in a resin sand mould promoted directional solidification and showed a nodularity decrease for increasing Si, for all the nodularity formulas and for the cooling rate range. Inoculating elements influenced the shape factors in thin wall castings, where Ca–Ba was better than simple Ca and Ca–RE could promote graphite at higher real perimeter and with lower shape factors. The correlation of the aspect of structure, graphite parameters and nodularity led to the conclusion that the nodularity formula according to ISO/WD 945-4-2015 (100% total area of Form VI and 90% of Form V), with SSF instead of RSF, appears to be better in High-Si/SiMo DI (especially for more than 4% Si), because it takes into account the presence of slightly irregular spheroidal graphite (with high real perimeter) at a high rate.
Stan et al. (Tue,) studied this question.