Abstract Lithium‐ion batteries currently suffer from low capacity and fast degradation under fast charging and/or low temperatures. In this work, a colloid liquid electrolyte (CLE) is designed, where the trace amount of lithium thiocarbonate (LTC) colloids in commercial carbonate electrolyte (1 m LiPF 6 in ethylene carbonate/dimethyl carbonate) not only boosts up σ Li+ but also improves the Li + transfer kinetics at LiNi 0.8 Co 0.15 Al 0.05 O 2 (NCA) cathode/electrolyte interface. The competitive coordination of LTCs with anions and solvents facilitates the dissociation of lithium salts and Li + decoupling, dramatically enhancing the σ Li+ (15 to 4.5 mS cm −1 at 30 and −20 °C, respectively); meanwhile, the desolvation process is accelerated. It demonstrates that LTC colloids induce an ≈5 nm ultrathin Li 2 CO 3 ‐rich cathode electrolyte interface and infuse the grain boundary of NCA particles, enhancing interfacial Li + transfer and inhibiting the particle cracks during cycling. Consequently, the Li||CLE||NCA battery delivers a maximum capacity of 135 mAh g −1 at a 10 C rate with 80% retention after 2000 cycles. Moreover, the fast‐charging capability under a sub‐zero environment is proved (122 mAh g −1 with 90% retention after 400 cycles at 2 C and −10 °C). This strategy for tailoring the interfacial charge transfer appears generalizable and can practically be extended to next‐generation energy‐storage systems.
Wang et al. (Thu,) studied this question.