Cr-segregation by spinodal decomposition and G-phase precipitation were observed in δ-ferrite of austenitic stainless steel welds thermally aged at 400 °C for up to 20,000 h. A reversion heat treatment (R-HT) at 550 °C for 1 h dissolved the Cr-segregation in the aged welds while some intermetallic precipitates were present. The double-loop electrochemical potentiokinetic reactivation (DL-EPR) analysis showed no significant differences among them. However, after selective etching of the austenite phase, the DL-EPR values of δ-ferrite phase steadily increased with aging time due to the growth of Cr-depleted regions by spinodal decomposition. The electrochemical behavior of δ-ferrite after R-HT condition was similar to that of unaged welds, indicating the intermetallic precipitates did not affect the corrosion resistance in this case. Overall, DL-EPR analysis of δ-ferrite phase provided better correlation with spinodal decomposition.
No takes yet. Share an insight, caveat, or question.
Subramanian et al. (2018) studied this question.
Synapse has enriched 10 related papers. Consider them for comparative context: