Efficient tailoring of upconversion emissions in lanthanide-doped nanocrystals is of great significance for extended optical applications. Here, we present a facile and highly effective method to tailor the upconversion selectivity by engineering the local structure of lanthanides in Na(x)REF(3+x) nanocrystals. The local structure engineering was achieved through precisely tuning the composition of nanocrystals, with different Na/RE (F/RE) ratio. It was found that the lattice parameter as well as the coordination number and local symmetry of lanthanides changed with the composition. A significant difference in the red to green emission ratio, which varied from 1.9 to 71 and 1.6 to 116, was observed for Na(x)YF(3+x):Yb,Er and Na(x)GdF(3+x):Yb,Er nanocrystals, respectively. Moreover, the local structure-dependent upconversion selectivity has been verified for Na(x)YF(3+x):Yb,Tm nanocrystals. In addition, the local structure induced upconversion emission from Er(3+) enhanced 9 times, and the CaF2 shell grown epitaxially over the nanocrystals further promoted the red emission by 450 times, which makes it superior as biomarkers for in vivo bioimaging. These exciting findings in the local structure-dependent upconversion selectivity not only offer a general approach to tailoring lanthanide related upconversion emissions but also benefit multicolor displays and imaging.
Dong et al. (Mon,) studied this question.