Probing the role of the first monolayer in the evolution of the film polymer microstructure is essential for the fundamental understanding of the charge carrier transport in polymeric field-effect transistors (FETs). The monolayer and its subsequent microstructure of a conjugated polymer poly(2,5-bis(3-alkylthiophen-2-yl)thieno[3,2-bthiophene), PBTTT] film were fabricated via solution deposition by tuning the dip-coating speed and were then studied as accumulation and transporting layers in FETs. Investigation of the microstructure of the layers prepared at different coating velocities revealed that the monolayer serves as an important base for further development of the film. Significant improvement of the charge carrier transport occurs only at a critical multilayer network density that establishes the required percolation pathways for the charge carriers. Finally, at a low dip-coating speed, the polymer chains are uniaxially oriented, yielding pronounced structural anisotropy and high charge carrier mobilities of 1.3 cm(2) V(-1) s(-1) in the alignment direction.
Wang et al. (Tue,) studied this question.