Cu-Sn-Ti metallic-bonded CBN (Cubic Boron Nitride) abrasives are widely applied in the precision grinding of superhard materials. However, their high density and high toughness easily lead to poor grain protrusion and inadequate self-sharpening. In this work, ceramic glass powder was incorporated to modify the Cu-Sn-Ti binder, thereby fabricating composite-bonded CBN abrasive blocks with qualified mechanical properties and excellent self-sharpening performance. Flexural strength of abrasive blocks and microhardness of composite binders were measured; microstructure was characterized, phase composition was analyzed by XRD, and tribological tests were carried out between CBN blocks and silicon nitride abrasives. The results indicate that at glass powder contents of 2.94–10.22 wt%, the flexural strength of CBN blocks decreases by 32.5–89.4%, and binder microhardness reduces by 26.5–58.3%. At high brazing temperature, Ti and Cu from Cu-Sn-Ti alloy react with Si and Al in glass powder at the interface to form new phases including Ti2O3, Ti5Si3 and Ti(Cu,Al)2, which facilitates favorable interfacial bonding among the alloy matrix, glass phase and CBN grains. With increasing glass powder content, the strength decline gradually slows down. The overall wear resistance of abrasive blocks declines. SEM observations on worn CBN blocks and their composite binders reveal the formation of micropores within glass-containing binders, accompanied by a shift in the fracture mode of CBN abrasives upon glass powder addition. Comprehensive experimental analysis indicates that the No.3 sample with 8.33 wt% glass powder possesses the optimal overall performance.
Zhang et al. (Thu,) studied this question.