Key points are not available for this paper at this time.
This in vitro study evaluated the survival rate and fracture resistance of maxillary central incisors restored with different post and core systems. The post and core systems investigated were a prefabricated high precious metal post with cast core (group A), zirconia post with a prefabricated bonded ceramic core (group B), and a resin-ceramic interpenetrating phase composite post (experimental) with a prefabricated bonded ceramic core (group C). The all-ceramic copings were cemented using Panavia 21 TC. In the group without coronoradicular reinforcement, the access cavity was closed with a light-cured composite in combination with a dentine-bonding agent (group D). Each specimen was intermittently loaded and thermocycled before final stress tests in a Zwick machine. The survival rates after 1,200,000 cycles in the artificial mouth were 90% (group A), 80% (group B), 60% (group C), and 100% (group D). Statistically significant differences were found between all groups with the exception of A and B, when failure during cyclic loading was included (Kruskal-Wallis multiple comparisons test). Samples restored with a cast post and core demonstrated more vertical root fractures. It was concluded that the preservation of both internal and external tooth structure is of utmost importance when restoring endodontically treated teeth. This in vitro study evaluated the survival rate and fracture resistance of maxillary central incisors restored with different post and core systems. The post and core systems investigated were a prefabricated high precious metal post with cast core (group A), zirconia post with a prefabricated bonded ceramic core (group B), and a resin-ceramic interpenetrating phase composite post (experimental) with a prefabricated bonded ceramic core (group C). The all-ceramic copings were cemented using Panavia 21 TC. In the group without coronoradicular reinforcement, the access cavity was closed with a light-cured composite in combination with a dentine-bonding agent (group D). Each specimen was intermittently loaded and thermocycled before final stress tests in a Zwick machine. The survival rates after 1,200,000 cycles in the artificial mouth were 90% (group A), 80% (group B), 60% (group C), and 100% (group D). Statistically significant differences were found between all groups with the exception of A and B, when failure during cyclic loading was included (Kruskal-Wallis multiple comparisons test). Samples restored with a cast post and core demonstrated more vertical root fractures. It was concluded that the preservation of both internal and external tooth structure is of utmost importance when restoring endodontically treated teeth. ErratumJournal of EndodonticsVol. 38Issue 3PreviewOliver Pontius and Jeffrey W. Hutter, authors of the article “Survival Rate and Fracture Strength of Incisors Restored with Different Post and Core Systems and Endodontically Treated Incisors without Coronoradicular Reinforcement” (J Endod 2002;2810:710–5), would like to add 3 coauthors to their article. The author order now reads: Pontius O, Nathanson D, Giordano R, Schilder H, Hutter JW. They would also like to add the following citation to their article: Strub JO, Pontius O, Koutayas S. Survival rate and fracture strength of incisiors restored with different post and core systems after exposure in the artificial mouth. Full-Text PDF
Pontius et al. (Tue,) studied this question.