Enhanced intrinsic biomechanical properties of osteoblastic mineralized tissue on roughened titanium surface

The biological mechanisms underlying bone-titanium integration and biomechanical properties of the integrated bone are poorly understood. This study assesses intrinsic biomechanical properties of mineralized tissue cultured on titanium having different surface topographies. The osteoblastic phenotypes associated with mineral deposition and collagen synthesis underlying the biomechanical modulation are also reported. Rat bone marrow-derived osteoblastic cells were cultured either on the machined titanium disc or acid-etched titanium disc. Nano-indentation study of day 28 culture revealed that the mineralized tissue on the acid-etched surface shows 3-3.5 times greater hardness than that on the machined surface (p < 0.01). Elastic modulus of the mineralized tissue was also 2.5-3 times greater on the acid-etched surface than on the machined surface (p < 0.01). After 28 days of culture, mineralized nodule area was significantly lower on the acid-etched surface than on the machined surface (p = 0.0105), while total calcium deposition did not differ between the two surfaces, indicating denser mineral deposition on the acid-etched surface. Osteopontin and osteocalcin gene expressions assayed by the reverse transcriptase-polymerase chain reaction were upregulated in the acid-etched titanium culture. Collagen synthesis measured by Sirius red stain-based colorimetry was 1.5-10 times higher on the acid-etched surface than on the machined surface in the initial culture period of day 1 to day 14 (p < 0.0001). The amount of collagen synthesis corresponded with the enhanced gene expression of prolyl 4-hydroxylase, a key enzyme for post-translational modification of collagen chains. Scanning electron microscopic images revealed that tissue cultured on the acid-etched titanium exhibited plate-like, compact surface morphology, while the tissue on the machined titanium appeared porous and was covered by fibrous and punctate structures. We conclude that culturing osteoblasts on rougher titanium surfaces enhances hardness and elastic modulus of the mineralized tissue, associated with condensed mineralization, accelerated collagen synthesis, and upregulated expression of selected bone-related genes.