Preparation of Stable ZrB₂-SiC-B₄C Aqueous Suspension for Composite Based Coating: Effect of Solid Content and Dispersant on Stability

ZrB 2 -SiC-B 4 C aqueous suspension has been prepared using poly(ethyleneimine) as a dispersant. Since increasing the solid content of suspension leads to high compaction and consequently low porosities through final coat, the effect of solid content has been studied. The dispersant and solid content were changed in the range of 0.3–1.5 wt.% and 45–55 vol.%, respectively, to assess the optimal conditions effect on stability and characteristics of suspension. Results of zeta potential measurements and rheological analysis at pH 7.8 showed that the composite suspension including 45 vol.% solid content and 1.5 wt.% dispersant was in stable state.