High Efficiency Nonfullerene Polymer Solar Cells with Thick Active Layer and Large Area

In this work, high‐efficiency nonfullerene polymer solar cells (PSCs) are developed based on a thiazolothiazole‐containing wide bandgap polymer PTZ1 as donor and a planar IDT‐based narrow bandgap small molecule with four side chains (IDIC) as acceptor. Through thermal annealing treatment, a power conversion efficiency (PCE) of up to 11.5% with an open circuit voltage ( V oc ) of 0.92 V, a short‐circuit current density ( J sc ) of 16.4 mA cm −2 , and a fill factor of 76.2% is achieved. Furthermore, the PSCs based on PTZ1:IDIC still exhibit a relatively high PCE of 9.6% with the active layer thickness of 210 nm and a superior PCE of 10.5% with the device area of up to 0.81 cm 2 . These results indicate that PTZ1 is a promising polymer donor material for highly efficient fullerene‐free PSCs and large‐scale devices fabrication.