Properties of InSbN grown on GaAs by radio frequency nitrogen plasma-assisted molecular beam epitaxy

We report the growth of InSbN on a lattice-mismatched GaAs substrate using radio frequency nitrogen plasma-assisted molecular beam epitaxy. The effects of a two-step thin InSb buffer layer grown at 330 and 380 °C and substrate temperature (270–380 °C) on the properties of the InSbN are studied. The crystalline quality of the InSbN is significantly improved by the two-step buffer layer due to defect suppression. The shifting in the absorption edge of the InSbN from ∼5 to 8 µm following an increase in the substrate temperature is correlated with the reduction in free carrier concentration from ∼10 18 to 10 16 cm −3 and increase in concentration of N substituting Sb from ∼0.2 to 1%. These results will be beneficial to those working on the pseudo-monolithic integration of InSbN detectors on a GaAs platform.