Curing and constitutive relationships for polyester mortar

The compressive and tensile properties of polyester mortar were studied under various curing conditions, temperature, and strain rate. The curing temperature was varied from room temperature to 80°C. The behavior of polyester mortar was studied using a uniform sand with strain rate and temperature varied between 0.01 to 6 percent strain per minute and 22°C and 120°C, respectively. The strength, failure strain, modulus and stress‐strain relationships of polyester mortar are influenced by the curing method, testing temperature, and strain rate to varying degrees. The influence of test variables on the mechanical properties of polyester mortar are quantified. Pretreating the aggregates with a silane coupling agent further enhances the compressive and tensile strength of the mortar. The compressive modulus and splitting tensile strength of polyester mortar are related to the compressive strength. A constitutive model is used to predict the compressive stress‐strain behavior of polyester mortar.