Ferroelectric Pb[Zr 0.25 T 0.37 (Mg 1/3 Nb 2/3 ) 0.38 ]O 3 thick films were prepared by a screen printing method on ZrO 2 ceramic substrates over the firing temperature range of 1100°C to 1300°C. The microstructures, ferroelectric properties and electric field-induced-strain properties of the thick films were examined in comparison with bulk ceramics. A large remanent polarization of 33.0 µC/cm 2 and a small coercive field of 6.5 kV/cm were obtained for the thick film fired at 1200°C. These values were comparable to those of bulk ceramics.