Synthesis of a cubic Ge3N4 phase at high pressures and temperatures

The two known phases of germanium nitride (Ge3N4) have hexagonal and trigonal symmetries and consist of three-dimensional networks of corner-connected Ge–N tetrahedra. A new cubic spinel phase (space-group Fd3m, a0=8.3 Å, Z=8, ρ=6.36 g/cm3) containing Ge–N octahedra and tetrahedra in a 2:1 ratio was synthesized from elemental germanium and molecular nitrogen starting materials in a laser-heated diamond-anvil cell above 14 GPa. This phase is isostructural to the recently discovered cubic spinel phase of Si3N4.