Nanoenergetic Composite of Mesoporous Iron Oxide and Aluminum Nanoparticles

Ordered mesoporous Fe2O3 was synthesized using cetyltrimethylammonium chloride (CTAC) and polyethylene glycol octadecyl ether (Brij 76) surfactant templates. The gel time was monitored as a function of the concentration ratio of precursor to the surfactant. As-prepared FeOOH gels were extracted in ethanol to remove the surfactant and calcined at 200–400°C for 6 h so that α-Fe2O3 is produced. The FTIR spectra of these gels reveal complete removal of surfactant and water impurities and the presence of Fe-O vibrations. TEM images show ordering of mesopores in the gels prepared using surfactant templating and no ordering of the pores in the gels prepared without surfactant. The gels after calcinations were mixed with aluminum nanoparticles to prepare nanoenergetic composites. The burn rate of the nanocomposites containing ordered mesoporous Fe2O3 mixed with Al nanoparticles was compared with the one containing Fe2O3 with no ordering of mesopores and Al nanoparticles.