High‐Performance Nanocomposites of Sodium Carboxymethylcellulose and Graphene Oxide

High‐performance nanocomposites of NaCMC with GO are produced by solution casting. FESEM images reveal a good homogeneous dispersion of GO in the NaCMC matrix. The composite formation is facilitated by H‐bonding interaction between GO and NaCMC. T g of the composites increases with increasing GO concentration. The storage modulus ( G ′) exhibits a maximum 174% increase over NaCMC at 1 wt% GO. The mechanical properties of the composites exhibit highest increase of tensile stress and Young's modulus of 188 ± 4% and 154 ± 11%, respectively, for 1 wt% GO. Analysis of Young's modulus ( E y ) data using the Halpin‐Tsai equation suggests that the E y data are close to the unidirectional orientation at >0.5 wt% GO, indicating more efficient load transfer at these compositions. magnified image