Calcium-deficient Hydroxyapatite as a Potential Sorbent for Strontium

A calcium (Ca)-deficient hydroxyapatite was investigated for its potential to remove Sr 2+ from environmentally relevant water. We conducted sorption tests on solutions containing magnesium ion (Mg 2+ ) and calcium ion (Ca 2+ ) as competing cations at a strontium ion (Sr 2+ ) concentration of 0.05 mmol/L. The Ca-deficient hydroxyapatite maintained a high Sr 2+ sorption ratio of above 80% in the presence of Mg 2+ and Ca 2+ at the concentrations between 0.1 and 1.0 mmol/L, whereas the stoichiometric hydroxyapatite showed a lower ratio even in the presence of small amounts of Mg 2+ and Ca 2+ (72% for Mg 2+ and 51% for Ca 2+ at 0.1 mmol/L). For solutions with various Sr 2+ concentrations between 0.01 and 10 mmol/L, Ca-deficient hydroxyapatite exhibited a higher Sr 2+ sorption ratio than stoichiometric hydroxyapatite. The bonding states of Sr 2+ on the Ca-deficient hydroxyapatite were evaluated by extended X-ray absorption fine structure measurements. The results indicated that there are specific sorption sites in Ca-deficient hydroxyapatite where Sr 2+ is stably and preferentially immobilized.